Study of the influence of load by friction of carbonaceous materials at high temperatures

Roshchin M.N., Krivosheev A.Yu.

Исследование влияния нагрузки при трении углеродосодержащих материалов при высоких температурах

Рощин М.Н., Кривошеев А.Ю.

Full text (Полный текст) PDF

Keywords: friction, coefficient of friction, load, high temperature tests, contact pressure, CCCM.

Ключевые слова: трение, коэффициент трения, нагрузка, высокотемпературные испытания, контактное давление, УУКМ.

Abstract. The work is devoted to high-temperature laboratory tribological tests of carbonaceous materials. It is established that at a temperature of 700 ° C and a load of 0.5 MPa the friction coefficient for samples of material "Hardcarb" less by 21% than that of the material "Angolan-2D", and at a load of 1.0 MPa the friction coefficient for samples of material "Hardcarb" less by 18% than that of the material "Angolan-2D".

Аннотация. Работа посвящена высокотемпературным лабораторным трибологическим испытаниям углеродосодержащих материалов. Установлено, что при температуре 700ºС и нагрузке 0,5МПа коэффициент трения для образцов из материала «Хардкарб» меньше на 21%, чем у материала «Арголон-2D», а при нагрузке 1,0МПа коэффициент трения для образцов из материала «Хардкарб» меньше на 18%, чем у материала «Арголон-2D».