Modification of surface friction cccm pairs of tin selenide for high temperatures
Roshchin M.N.
Модификация поверхности трения уукм парами селенида олова для работы при высоких температурах
Рощин М.Н.
Full text (Полный текст) PDF
Keywords: friction, coefficient of friction, load, high temperature tests, contact pressure, CCCM.
Ключевые слова: трение, коэффициент трения, нагрузка, высокотемпературные испытания, контактное давление, УУКМ.
Abstract. The work is devoted to high-temperature laboratory tribological tests of carbon-carbon composite material and its modification. It is established that a modified friction surface CCCM in the environment of SnSe-PTFE mated with steel 40H13 at a temperature 500ºС and a load of 1.0 MPa, the friction coefficient is 5.6 times less than that of the CCCM, and at a load of 0.5 MPa the friction coefficient is 5.9 times less than that of CCCM.
Аннотация. Работа посвящена высокотемпературным лабораторным трибологическим испытаниям углерод-углеродного композиционного материала и его модификации. Установлено, что модифицированная поверхность трения УУКМ в среде SnSe-ПТФЭ в паре со сталью 40Х13 при температуре 500ºС и нагрузке 1,0 МПа имеет коэффициент трения в 5,6 раз меньше, чем у УУКМ, а при нагрузке 0,5МПа коэффициент трения в 5,9 раз меньше, чем у УУКМ.