JARiNS. – 2019. – № 7
https://doi.org/10.26160/2572-4347-2019-7-15-18
The study of the influence of surface modification of carbon-containing friction materials on the friction coefficient
Roshchin M.N.
Изучение влияния модификации поверхности трения углеродосодержащих материалов на коэффициент трения
Рощин М.Н.
Full text (Полный текст) PDF
Keywords: friction, coefficient of friction, load, high temperature tests, contact pressure, CCCM.
Ключевые слова: трение, коэффициент трения, нагрузка, высокотемпературные испытания, контактное давление, УУКМ.
Abstract. The work is devoted to high-temperature laboratory tribological tests of ССCM and its modification. It was found that the modified surface of friction ССCM treated in Se-PTFE at a temperature of 600°C and a load of 1.0 MPa has a friction coefficient of 40X13 steel samples in 2,4 and 3,3 times less than the samples treated in SnSe-PTFE and PTFE, respectively.
Аннотация. Работа посвящена высокотемпературным лабораторным трибологическим испытаниям УУКМ и его модификации. Установлено, что модифицированная поверхность трения УУКМ, обработанная в среде Se-ПТФЭ, при температуре 600ºС и нагрузке 1,0МПа имеет коэффициент трения образцов по стали 40Х13 в 2,4 и 3,3 раза меньше, чем образцов, обработанных в среде SnSe-ПТФЭ и ПТФЭ соответственно.