JARiNS. – 2019. – № 6
https://doi.org/10.26160/2572-4347-2019-6-29-32
Bending strength of ceramics based on zirconium dioxide at high temperatures
Alisin V.V.
Прочность на изгиб керамики на основе диоксида циркония в условиях высоких температур
Алисин В.В.
Full text (Полный текст) PDF
Keywords: bending tests of materials, high temperature tests, ceramics, zirconium dioxide, bending strength.
Ключевые слова: испытания материалов на изгиб, высокотемпературные испытания, керамика, диоксид циркония, прочность на изгиб.
Abstract. The article is devoted to the description of high-temperature bending test of ceramics based on partially stabilized zirconium dioxide. The experiments were performed according to the three-point bending scheme. It is established that the bending strength with temperature increase of 700 to 1500 0C falls significantly, but remains within acceptable limits for use in high-temperature friction units.
Аннотация. Статья посвящена описанию высокотемпературного испытания на изгиб керамики на основе частично стабилизированного диоксида циркония. Эксперименты выполнены по схеме трехточечного изгиба. Установлено, что прочность при изгибе с повышением температуры 700 до 1500 0C существенно падает, но остается в допустимых пределах для применения в высокотемпературных узлах трения.