Study of physical and mechanical characteristics of structural steels during fatigue testing

Pishchov M.N., Belsky S.E.

Keywords: microhardness, operation, reliability, steel, surface hardening, fatigue characteristics, surface roughness, time, temperature.

Abstract. This article examines changes in a number of physical and mechanical properties of structural steel during fatigue testing. The tests were conducted under alternating bending conditions using loading frequencies of 0.3, 3.0, 9.0, and 18.0 kHz on samples surface-hardened by borosilicate coating. It is shown that the microhardness and dislocation density of the studied material increase during the initial stage of testing, indicating the development of a hardening process followed by softening at the final stage.

Изучение физико-механических характеристик конструкционных сталей при проведении усталостных испытаний

Пищов М.Н., Бельский С.Е.

Ключевые слова: микротвердость, эксплуатация, надежность, сталь, поверхностное упрочнение, усталостные характеристики, шероховатость поверхности, время, температура.

Аннотация. В статье изучены изменения ряда физико-механических характеристик конструкционной стали при проведении усталостных испытаний. Испытания проводились в условиях знакопеременного изгиба с использованием частот нагружения 0,3; 3,0; 9,0 и 18,0 кГц на образцах прошедших поверхностное упрочнение боросилицированием. Показано, что микротвердость и плотность дислокаций исследованного материала на начальном этапе испытаний возрастают, что характеризует развитие процесса упрочнения материала, сменяющегося разупрочнением на заключительном этапе.