Analysis of the heat treatment modes influence on the life of the tool for hot forming
Yakubovich E.A.
Анализ влияния режимов термической обработки на стойкость инструмента для горячей штамповки
Якубович Е.А.
Full text (Полный текст) PDF
Keywords: die steels, tool life, heat treatment, extrusion stamping, crank press, quasi-analogue tests, pilot testing.
Ключевые слова: штамповые стали, стойкость инструмента, термическая обработка, штамповка выдавливанием, кривошипный пресс, квазианалоговые испытания, опытно-промышленная проверка.
Abstract. The article analyzes the dependence of tool life during stamping by extrusion on the choice of hardening and tempering temperatures. The expediency of increasing the hardening temperature for the investigated steels with a corresponding adjustment of the tempering temperature has been substantiated. The optimum temperature for quenching dies for hot extrusion is the temperature at which a grain of 7 - 8 points is obtained without a drop in impact strength. Based on the results of comparative industrial tests of matrices made of various steels for hot extrusion, it can be concluded that complex alloyed steels have a higher performance than steels of the 3X2V8F and 5XNV types.
Аннотация. В статье выполнен анализ зависимости стойкости инструмента при штамповке выдавливанием от выбора температур закалки и отпуска. Обоснована целесообразность повышения температуры закалки для исследованных сталей при соответствующей корректировке температуры отпуска. Оптимальной температурой закалки штампов для горячего выдавливания является температура, при которой получается зерно 7 – 8 балла без падения ударной вязкости. На основании результатов сравнительных опытно-промышленных испытаний матриц из различных сталей для горячего выдавливания можно сделать вывод, что комплексно легированные стали обладают более высокой работоспособностью, чем стали типа 3Х2В8Ф и 5ХНВ.